During a $$TIG$$ welding process, the arc current and arc voltage were $$50$$ $$A$$ and $$60$$ $$V,$$ respectively, when the welding speed was $$150$$ $$mm/min.$$ In another process, the $$TIG$$ welding is carried out at a welding speed of $$120mm/min$$ at the same arc welding voltage and heat input to the material so that weld quality remains the same. The welding current (in $$A$$) for this process is

A butt weld joint is developed on steel plates having yield and ultimate tensile strength of $$500$$ $$MPa$$ and $$700$$ $$MPa,$$ respectively. The thickness of the plates is $$8mm$$ and width is $$20mm.$$ Improper selection of welding parameters caused an undercut of $$3mm$$ depth along the weld. The maximum transverse tensile load (in $$kN$$) carrying capacity of the developed weld joint is _________________

For spot welding of two steel sheets (base metal) each of $$3$$ $$mm$$ thickness, welding current of $$10000$$ $$A$$ is applied for $$0.2$$ $$s$$. The heat dissipated to the base metal is $$1000J.$$ Assuming that the heat required for melting $$1m{m^3}$$ volume of steel is $$20J$$ and interfacial contact resistance between sheets is $$0.0002$$$$\Omega $$, the volume (in $$m{m^3}$$) of weld nugget is _____________

In a $$DC$$ $$arc$$ welding operating, the length characteristic was obtained as $${V_{arc}} = 20 + 5l$$ where the $$arc$$ length $$l$$ was varied between $$5mm$$ and $$7mm.$$ Here $${V_{arc}}$$ denotes the arc voltage in volts. The $$arc$$ current was varied from $$400A$$ to $$500A.$$ Assuming linear power source characteristic, the open circuit voltage and the short circuit current for the welding operation are