A $$DC$$ welding power source has a linear voltage-current $$(V$$-$$I)$$ characteristic with open circuit voltage of $$80V$$ and a short circuit current of $$300A.$$ For maximum arc power, the current (in Amperes) should be set as _______________

A butt weld joint is developed on steel plates having yield and ultimate tensile strength of $$500$$ $$MPa$$ and $$700$$ $$MPa,$$ respectively. The thickness of the plates is $$8mm$$ and width is $$20mm.$$ Improper selection of welding parameters caused an undercut of $$3mm$$ depth along the weld. The maximum transverse tensile load (in $$kN$$) carrying capacity of the developed weld joint is _________________

For spot welding of two steel sheets (base metal) each of $$3$$ $$mm$$ thickness, welding current of $$10000$$ $$A$$ is applied for $$0.2$$ $$s$$. The heat dissipated to the base metal is $$1000J.$$ Assuming that the heat required for melting $$1m{m^3}$$ volume of steel is $$20J$$ and interfacial contact resistance between sheets is $$0.0002$$$$\Omega $$, the volume (in $$m{m^3}$$) of weld nugget is _____________

In a $$DC$$ $$arc$$ welding operating, the length characteristic was obtained as $${V_{arc}} = 20 + 5l$$ where the $$arc$$ length $$l$$ was varied between $$5mm$$ and $$7mm.$$ Here $${V_{arc}}$$ denotes the arc voltage in volts. The $$arc$$ current was varied from $$400A$$ to $$500A.$$ Assuming linear power source characteristic, the open circuit voltage and the short circuit current for the welding operation are