A weld is made using $$MIG$$ welding process with the following welding parameters: Current: $$200A;$$ Voltage: $$25V;$$ Welding speed: $$18$$ $$cm/min;$$ wire diameter: $$1.2$$ $$mm;$$ Wire feed rate: $$4$$ $$m/min;$$ Thermal efficiency of the process: $$65\% $$

The heat input per unit length of the weld in $$kJ/cm$$ is:

A weld is made using $$MIG$$ welding process with the following welding parameters: Current: $$200A;$$ Voltage: $$25V;$$ Welding speed: $$18$$ $$cm/min;$$ wire diameter: $$1.2$$ $$mm;$$ Wire feed rate: $$4$$ $$m/min;$$ Thermal efficiency of the process: $$65\% $$

The area of cross section of weld bead in $$m{m^2}$$ is:

The cold cracking susceptibility of the heat affected zone in an arc weld is influenced by
$$P.$$ Entraped hydrogen,
$$Q.$$ Residual stresses
$$R.$$ Marternsitic transformation
$$S.$$ Slag inclusion

Match List - I (welding defects) with List - II (causes) and select the correct answer using the codes given below the lists