Match List - I (welding defects) with List - II (causes) and select the correct answer using the codes given below the lists

A weld is made using $$MIG$$ welding process with the following welding parameters: Current: $$200A;$$ Voltage: $$25V;$$ Welding speed: $$18$$ $$cm/min;$$ wire diameter: $$1.2$$ $$mm;$$ Wire feed rate: $$4$$ $$m/min;$$ Thermal efficiency of the process: $$65\% $$

The heat input per unit length of the weld in $$kJ/cm$$ is:

A weld is made using $$MIG$$ welding process with the following welding parameters: Current: $$200A;$$ Voltage: $$25V;$$ Welding speed: $$18$$ $$cm/min;$$ wire diameter: $$1.2$$ $$mm;$$ Wire feed rate: $$4$$ $$m/min;$$ Thermal efficiency of the process: $$65\% $$

The area of cross section of weld bead in $$m{m^2}$$ is:

Tool life equation for two tools under consideration are as follows

$$\eqalign{ & HSS:\,\,\,\,\,\,\,\,\,\,\,\,\,V{T^{0.2}} = 150 \cr & Carbide:\,\,\,\,\,\,V{T^{0.3}} = 250 \cr} $$
Where $$V$$ is the cutting speed in $$m/min$$ and $$T$$ is the tool life in $$min.$$ The breakdown cutting speed above which the carbide tool will be beneficial is