In resistance welding, heat is generated due to the resistance between

A $$900$$ $$mm$$ long steel plate is welded by manual metal arc welding process using welding current of $$150$$ $$A,$$ arc voltage of $$20$$ $$V$$ and welding speed of $$300$$ $$mm/min.$$ If the process efficiency of is $$0.8$$ and surface resistance is $$36$$ micro-ohm, the heat input will be

A weld is made using $$MIG$$ welding process with the following welding parameters: Current: $$200A;$$ Voltage: $$25V;$$ Welding speed: $$18$$ $$cm/min;$$ wire diameter: $$1.2$$ $$mm;$$ Wire feed rate: $$4$$ $$m/min;$$ Thermal efficiency of the process: $$65\% $$

The heat input per unit length of the weld in $$kJ/cm$$ is:

A weld is made using $$MIG$$ welding process with the following welding parameters: Current: $$200A;$$ Voltage: $$25V;$$ Welding speed: $$18$$ $$cm/min;$$ wire diameter: $$1.2$$ $$mm;$$ Wire feed rate: $$4$$ $$m/min;$$ Thermal efficiency of the process: $$65\% $$

The area of cross section of weld bead in $$m{m^2}$$ is: