A $$80$$ $$mm$$ thick steel plate with $$400$$ $$mm$$ width is rolled to $$40mm$$ thickness in $$4$$ passes with equal reduction in each pass, by using rolls of $$800mm$$ diameter. Assuming the plane-strain deformation, what is the minimum coefficient of friction required for unaided rolling to be possible?

In a single pass rolling process using $$410mm$$ diameter steel rollers, a strip of width $$140mm$$ and thickness $$8mm$$ undergoes $$10\% $$ reduction of thickness. The angle of bite in radians is

In multi-pass operation, a round bar of $$10$$ $$mm$$ diameter and $$100$$ $$mm$$ length is reduced in cross-section by drawing it successively through a series of seven dies of decreasing exit diameter. During each of theses drawing operations, the reduction in cross-sectional area is $$35\% $$. The yield strength of the material is $$200$$ $$MPa.$$ Ignore strain hardening.

The total true strain applied and the final length (in $$mm$$), respectively, are

In multi-pass operation, a round bar of $$10$$ $$mm$$ diameter and $$100$$ $$mm$$ length is reduced in cross-section by drawing it successively through a series of seven dies of decreasing exit diameter. During each of theses drawing operations, the reduction in cross-sectional area is $$35\% $$. The yield strength of the material is $$200$$ $$MPa.$$ Ignore strain hardening.

Neglecting friction and redundant work, the force (in $$kN$$) required for drawing the bar through the first die, is