Which of the following powders should be fed for effective oxy-fuel cutting of stainless steel

A weld is made using $$MIG$$ welding process with the following welding parameters: Current: $$200A;$$ Voltage: $$25V;$$ Welding speed: $$18$$ $$cm/min;$$ wire diameter: $$1.2$$ $$mm;$$ Wire feed rate: $$4$$ $$m/min;$$ Thermal efficiency of the process: $$65\% $$

The heat input per unit length of the weld in $$kJ/cm$$ is:

A weld is made using $$MIG$$ welding process with the following welding parameters: Current: $$200A;$$ Voltage: $$25V;$$ Welding speed: $$18$$ $$cm/min;$$ wire diameter: $$1.2$$ $$mm;$$ Wire feed rate: $$4$$ $$m/min;$$ Thermal efficiency of the process: $$65\% $$

The area of cross section of weld bead in $$m{m^2}$$ is:

In certain machining operation with a cutting speed of $$50$$ $$m/min,$$ tool life of $$45$$ minutes was observed, when the cutting speed was increased to $$100$$ $$m/min,$$ the tool life decreased to $$10$$ minutes. The cutting speed for maximum productivity, if tool change time is $$2$$ minutes is