In a single pass flat rolling operation, a $$400mm$$ wide steel strip having a thickness of $$10mm$$ is reduced to $$8mm$$ by using a roll of $$600mm$$ diameter.

The roll-strip contact length is

In a single pass flat rolling operation, a $$400$$ $$mm$$ wide steel strip having a thickness of $$10mm$$ is reduced to $$8$$ $$mm$$ by using a roll of $$600mm$$ diameter.

Considering the situation for a maximum draft of the process, what is the coefficient of friction?

Calculate the minimum number of hot rolling passes necessary to reduce an ingot of $$200mm$$ thickness to $$100mm$$ thickness in two high reversible rolling mill with roll diameter is $$500$$ $$mm.$$ The coefficient of friction between the rolls and the hot material is assumed as $$0.20.$$

A steel wire of length $$100$$ $$m$$ and diameter $$12.214$$ $$mm$$ is drawn to a final diameter of $$10mm.$$ Tensile tests of specimen made before and after the drawing operation gave yield stress as $$200$$ $$MPa$$ and $$400$$ $$MPa$$ respectively,

The length of drawn wire is